Home / Products / Nickel Alloys / Inconel 601 / ASTM B166 Inconel 601 Wire
Inconel 601 (UNS: N06601, Werkstoff Nr.: 2.4851)
Inconel 601 is a nickel-chromium alloy used for applications that require resistance to corrosion and heat. This nickel alloy stands out due to its resistance to high temperature oxidation, remaining highly resistant to oxidation through 2200° F. Alloy 601 develops a tightly adherent oxide scale which resists spalling even under conditions of severe thermal cycling. This nickel alloy has good high temperature strength, and retains its ductility after long service exposure. It has good resistance to aqueous corrosion, high mechanical strength, and is readily formed, machined and welded. Inconel 601’s properties make it a material of broad utility in fields like thermal processing, chemical processing, pollution control, aerospace, and power generation. However, alloy 601 is not suggested for use in strongly reducing, sulfur bearing environments.
ASTM B166 Inconel 601 Wire
Specifications
Standards |
Designation |
ASTM |
B 166 |
ASME |
SB 166 |
UNS |
N06601 |
Werkstoff Nr. |
2.4851 |
Sizes |
Availability |
0.4mm |
|
0.5mm |
|
0.8mm |
|
1mm |
|
1.2mm |
|
1.6mm |
|
2mm |
|
2.5mm |
|
3mm |
|
4mm |
|
5mm |
|
Dimensions
Inconel 601 is a nickel-chromium-iron alloy. Inconel 601 is a general purpose engineering material that require resistance to heat & corrosion. Inconel 601 has outstanding resistance to high temperature oxidation.
Chemical Composition
|
Inconel 601 |
Ni |
58.0 – 63.0 |
Cr |
21.0 – 25.0 |
Fe |
Balance |
Al |
1.0 – 1.7 |
C |
0.10 max |
Mn |
1.0 max |
S |
0.015 max |
Si |
0.5 max |
Cu |
1.0 max |
Mechanical & Physical Properties – Inconel 601
Density |
8.1 g/cm3 |
Melting Point |
1411 °C (2571 °F) |
Tensile Strength |
Psi – 80,000 , MPa – 550 |
Yield Strength (0.2%Offset) |
Psi – 30,000 , MPa – 205 |
Elongation |
30 % |
Subcategory: Metal; Nickel Base; Superalloy
Key Words: Inconel 601, Nickel-Chromium Alloy; Werkstoff Nr. 2.4851, UNS N06601; ASME Boiler Code Section VIII; AMS 5715, AMS 5870; ASTM B166, ASTM B167, ASTM B168; DIN 17742, 17750 - 17752
Component Wt. %
Al 1 - 1.7
C Max 0.1
Cr 21 - 25 |
Component Wt. %
Cu Max 1
Fe 13
Mn Max 1
58 - 63 |
Component Wt. %
Ni
S Max 0.015
Si Max 0.5 |
Standard product forms are round, flats, forging stock, pipe, tube, plate, sheet, strip, and wire. |
Electrical Properties |
Electrical Resistivity |
0.000119 ohm-cm |
0.000119 ohm-cm |
|
Magnetic Permeability |
1.003 |
1.003 |
at 200 oersted (15.9 kA/m) |
Curie Temperature |
Max -196 °C |
Max -321 °F |
|
Thermal Properties |
CTE, linear 20°C |
13.75 µm/m-°C |
7.64 µin/in-°F |
20-100°C |
Heat Capacity |
0.448 J/g-°C |
0.107 BTU/lb-°F |
|
Thermal Conductivity |
11.2 W/m-K |
77.7 BTU-in/hr-ft²-°F |
|
Melting Point |
1360 - 1411 °C |
2480 - 2570 °F |
|
Solidus |
1360 °C |
2480 °F |
|
Liquidus |
1411 °C |
2570 °F |
|
Main Export Market
- Eastern Europe
- North America
- Mid East/Africa
- Central/South America
- Asia
- Western Europe
- Australasia
- UAE
Sales Locations
U.A.E,
Oman,
Saudi Arabia,
Qatar,
Bahrain,
Egypt,
Turkey
Singapore,
Thailand,
Malaysia
Indonesia
Poland
Italy
Portugal
Spain
Brazil
Chile
Venezuela
Costa Rica
USA
Canada
Angola
Sri Lanka
Russia